Fabrication of biocomposite materials with polycaprolactone and activated carbon extracted from agricultural waste
Loading...
Access rights
openAccess
publishedVersion
URL
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
This publication is imported from Aalto University research portal.
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Date
Major/Subject
Mcode
Degree programme
Language
en
Pages
14
Series
Colloids and Surfaces A: Physicochemical and Engineering Aspects, Volume 702, issue Part 2
Abstract
In this study, activated carbon was extracted from a source of agricultural waste (wheat straw) through a chemical activation process and blended with polycaprolactone (PCL) to fabricate new biocomposite materials. Three distinct types of activated carbon, designated as C1, C2, and C3 were obtained by varying the ratio of the activation agent and wheat straw and different drying conditions. Through a comprehensive array of analytical techniques, including FTIR, XRD, BET, EDS, and FE-SEM, we determined the optimal experimental method for extracting activated carbon from wheat straw and identified the most effective type of activated carbon (C3). Based on these analyses, C3 exhibits the highest carbon content, the greatest specific surface area (386.47 m2/g), and the highest total pore volume (0.2596 cm3/g). By blending polycaprolactone with the optimal activated carbon (at concentrations of 1, 3, and 5 wt%), biocomposite samples were fabricated. The results of FTIR indicate that the biocomposite materials containing 1, 3, and 5 wt% of activated carbon exhibit no disturbing peaks. However, the sample PCL-C,1 wt%, shows significant increases in the intensity of observed peaks. XRD analyses of the fabricated biocomposite samples illustrate that the sample containing 1 wt% of activated carbon has a greater tendency for crystallization compared to the other samples. Morphological analysis of the biocomposites and the dispersion of carbon particles within them demonstrate the least amount of agglomeration in the sample with an activated carbon concentration of 1 wt%. Upon assessing the mechanical properties of biocomposites, the same sample (1 wt% of C3) demonstrates more favorable characteristics than the other samples. Furthermore, a contact angle test was conducted to gauge the biocomposite hydrophilicity, revealing a 7 degree increase in contact angle for the sample with an activated carbon concentration of 1 wt% compared to the pure PCL sample. Thermal gravimetric analysis (TGA) and differential scanning calorimetry (DSC) were used to examine the weight loss, degradation temperature, melting temperature, and glass transition temperature of the synthesized materials. These analyses indicate a marginal augmentation in both melting and glass transition temperatures for the sample with an activated carbon concentration of 1 wt%.Description
Keywords
Other note
Citation
Mollaei, M, Karbasi, F, Sharifi Haddad, A & Baniasadi, H 2024, 'Fabrication of biocomposite materials with polycaprolactone and activated carbon extracted from agricultural waste', Colloids and Surfaces A: Physicochemical and Engineering Aspects, vol. 702, no. Part 2, 135175. https://doi.org/10.1016/j.colsurfa.2024.135175