Impact of Inherent Design Limitations for Cu–Sn SLID Microbumps on Its Electromigration Reliability for 3D ICs
Loading...
Access rights
openAccess
publishedVersion
URL
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
This publication is imported from Aalto University research portal.
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
Date
2023-01-01
Major/Subject
Mcode
Degree programme
Language
en
Pages
8
Series
IEEE Transactions on Electron Devices, Volume 70, issue 1, pp. 222-229
Abstract
Continuous scaling of package architectures requires small volume and high-density microbumps in 3D stacking, which often result in solders fully transforming to intermetallic compounds (IMCs). Cu-Sn solid-liquid interdiffusion (SLID) bonding is an attractive technology where the μ bumps are fully composed of IMCs. In this work, test structures made up of Cu3Sn IMC μ bump with a lateral dimension of 25 μm × 25 μm and 50 μm × 50 μm, respectively, were manufactured on a pair of 4-inch Si wafers demonstrating wafer-level bonding capability. Electromigration (EM) tests were performed for accelerated conditions at a temperature of 150 °C for various current densities ranging from ≈2 × 104 to 1 × 105 A/cm2. Scanning electron microscopy (SEM) and elemental dispersive spectroscopy (EDS) were employed to characterize the as-fabricated test structures. Due to Sn squeeze out, Cu3Sn was formed at undesired location at the upper Cu trace. Both nondestructive [lock-in thermography (LiT)] and destructive techniques were employed to analyze the failure locations after EM tests. It was observed that the likelihood of failure spots is the current crowding zone along the interconnects in 3D architectures, which gets aggravated due to the formation of Cu3Sn in undesirable locations. Thermal runaway was observed even in Cu3Sn, which has been shown to be EM-resistant in the past, thus underlining inherent design issues of μ bumps utilizing SLID technology.Description
Keywords
Three-dimensional displays, Resistance, Current density, Bonding, Reliability, Scanning electron microscopy, Proximity effects
Other note
Citation
Tiwary, N, Ross, G, Vuorinen, V & Paulasto-Kröckel, M 2023, ' Impact of Inherent Design Limitations for Cu–Sn SLID Microbumps on Its Electromigration Reliability for 3D ICs ', IEEE Transactions on Electron Devices, vol. 70, no. 1, 9969996, pp. 222-229 . https://doi.org/10.1109/TED.2022.3224892