Neutron Diffraction Study of the Martensitic Transformation and Chemical Order in Heusler Alloy Ni1.91Mn1.29Ga0.8
Loading...
Access rights
openAccess
URL
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
This publication is imported from Aalto University research portal.
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Date
2015
Major/Subject
Mcode
Degree programme
Language
en
Pages
5
853-857
853-857
Series
Materials Today: Proceedings, Volume 2, issue Supplement 3
Abstract
Heusler alloys of Ni-Mn-Ga compositions demonstrate ferromagnetic shape memory effect in the martensitic state. The transformation temperature and the chemical order depend strongly on the composition. In the current work, the structure and chemical order of the martensitic phase of Ni1.91Mn1.29Ga0.8 were studied using neutron diffraction; the diffraction pattern was refined using the FullProf software. It was determined that the structural transition occurs around 330 K. At room temperature, 300 K, which is below the martensite transformation temperature, all the Bragg reflections can be described by a monoclinic lattice with a symmetry of space group P 1 2/m 1 and lattice constants of a = 4.23047(7) [Å], b = 5.58333(6) [Å], c = 21.0179(2) [Å], beta = 90.328(1). The chemical order is of critical importance in these alloys, and it was previously studied at 363 K. Analysis of the neutron diffraction in the monoclinic phase shows that the chemical order is maintained during the martensitic transformation.Description
Keywords
Chemical Order, Ni-Mn-Ga alloy, Magnetic Shape Memory, Neutron Diffraction, Rietveld Method, Structure Refinement
Other note
Citation
Ari-Gur , P , Garlea , V O , Cao , H , Ge , Y , Aaltio , I , Hannula , S-P & Koledov , V 2015 , ' Neutron Diffraction Study of the Martensitic Transformation and Chemical Order in Heusler Alloy Ni 1.91 Mn 1.29 Ga 0.8 ' , Materials Today: Proceedings , vol. 2 , no. Supplement 3 , pp. 853-857 . https://doi.org/10.1016/j.matpr.2015.07.416