Increased surface recombination in crystalline silicon under light soaking due to Cu contamination
Loading...
Access rights
openAccess
acceptedVersion
URL
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
This publication is imported from Aalto University research portal.
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
Date
Major/Subject
Mcode
Degree programme
Language
en
Pages
7
Series
Solar Energy Materials and Solar Cells, Volume 232
Abstract
Light-induced degradation (LID) can occur in crystalline silicon (Si) due to increased recombination in the bulk or at the surfaces. As an example, copper (Cu) is a contaminant that reportedly causes LID in the bulk of Si under illumination. In this article, we show that Cu contamination can also increase recombination at the surface under illumination using surface saturation current density (J 0) analysis. More specifically, in the presence of Cu we observed that J 0 increased from 14 fA/cm 2 to 330 fA/cm 2 in SiO 2 passivated Float Zone (FZ) Si, and from 11 fA/cm 2 to 200 fA/cm 2 in corresponding Czochralski (Cz) Si after illumination under an LED lamp (0.6 Suns, 80 °C). In reference samples without Cu contamination, the J 0 was unaffected. These results demonstrate that a significant increase in surface recombination is possible without the presence of hydrogen. Furthermore, hydrogen was not seen to affect the Cu-induced surface degradation as similar experiments made with hydrogenated silicon nitride (SiN x:H) did not show further increase in J 0. However, the timescale of the observed degradation was relatively fast (hours) indicating that Cu-induced surface degradation is a separate phenomenon from the earlier reported surface-related degradation.Description
avaa käsikirjoitus, kun julkaistu
Other note
Citation
Rauha, I TS, Soeriyadi, A H, Kim, M, Yli-Koski, M, Wright, B, Vähänissi, V, Hallam, B J & Savin, H 2021, 'Increased surface recombination in crystalline silicon under light soaking due to Cu contamination', Solar Energy Materials and Solar Cells, vol. 232, 111360. https://doi.org/10.1016/j.solmat.2021.111360