Interaction effect of adjacent small defects on the fatigue limit of a medium carbon steel
Loading...
Access rights
openAccess
acceptedVersion
URL
Journal Title
Journal ISSN
Volume Title
A1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä
This publication is imported from Aalto University research portal.
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
View publication in the Research portal (opens in new window)
View/Open full text file from the Research portal (opens in new window)
Other link related to publication (opens in new window)
Date
Major/Subject
Mcode
Degree programme
Language
en
Pages
15
Series
Fatigue and Fracture of Engineering Materials and Structures, Volume 40, issue 1, pp. 130-144
Abstract
Structural steels contain various material irregularities and natural defects which cause local stress concentrations from which fatigue cracks tend to initiate. Two defects in close proximity to each other may affect local stress distributions, and thus, begin to interact. In this paper, the effect of interacting small cracks on the fatigue limit is systematically investigated in a medium carbon steel. The growth of interacting cracks, as well as the characteristics of non-propagating cracks and microstructural aspects, was closely examined via the plastic replica method. It was found that although the fatigue limit is essentially controlled by the mechanics of interacting cracks, based on their configuration, the local microstructure comprised ferrite and pearlite has a statistical scatter effect on the behaviour of interacting cracks and non-propagating thresholds. With respect to the fatigue limit, when two defects were in close proximity, they behaved as a larger single defect. However, with greater spacing between defects, rather than mechanical factors, it is the local microstructure which determines the location and characteristics of non-propagating cracks.Description
Other note
Citation
Åman, M, Okazaki, S, Matsunaga, H, Marquis, G B & Remes, H 2017, 'Interaction effect of adjacent small defects on the fatigue limit of a medium carbon steel', Fatigue and Fracture of Engineering Materials and Structures, vol. 40, no. 1, pp. 130-144. https://doi.org/10.1111/ffe.12482