Pipe-to-pipe friction welding of dissimilar Al-SS joints for cryogenic applications

Abstract

In the present investigation, dissimilar materials such as AA6063 and SS304L having pipe dimensions of 60.33 mm outer diameter and 3.9 mm wall thickness were friction-welded with different conditions of process parameters. Nondestructive tests such as radiography test (RT) and liquid penetration test (LPT) were carried out on the welded pipes in order to qualify weld joint. Thermal shock test and helium leak tests were performed on the successful welded samples in order to check its ability to work with cryogenic application. The results revealed that the pipe-to-pipe configuration of dissimilar Al–SS joints was produced successfully by friction welding using continuous drive. There were no defects presented in the joint area as revealed by RT and LPT. Thermal shock test and helium leak tests have also confirmed the soundness of joints. Higher deformation of Al base material results in the huge flash formation of Al that results in the sleeve formation of Al pipe on SS pipe. The helium leak test has confirmedthe soundness of joints without any defects after its testing at 1.2 psi pressure. More than 60% of joint efficiency was obtained from Al–SS friction-welded joints.